Base oil SAE 10/95

 

 

 

Value

 

 

Requirements

Units

Minimum

Maximum

Typical

Testing methods

Appearance in temperature of 20oC

-

 

 

transparent, without any suspension

visual

 

Structural viscosity in the temp. of -20oC

mPa.s

 

 

2600

PN-88C/04150

Kinetic viscosity in the temp. of100oC not lower than

mm2/s

5,2

5,9

5,52

PN-EN ISO3104

ASTM D 445

Kinetic viscosity in the temp. of40oC

mm2/s

 

 

34

PN-EN ISO3104

ASTM D 445

Viscosity index not lower than

-

95

 

96

PN-79/C04013

ASTM D 2270

Flow temperature not higher than

oC

 

-15

-15

ASTM D 5950

ASTM D 5985

ASTM D 97

The ignition temperature not lower than

oC

210

 

230

PN EN ISO 2592

ASTM D 92

Residue after coking not higher than

%(m/m)

 

0,03

no

PN EN ISO 10370

ASTM D 4530

The acid value not higher than

mgKOH/g

 

0,05

0,014

PN-88/C04049

Residue after incineration not more than

%(m/m)

 

0,005

no

PN EN ISO 6245

ASTM D 482

Water content

%(m/m)

 

 

no

PN EN ISO 12937

ASTM D 6304

Corroding action in temp. of100oC in 3h time, on copper plates

Corrosion ratio

 

1

1

PN EN ISO 2160

ASTM D 130

Volatile matter content by Noack’s method

%(m/m)

 

15

11

PN-C-04124:2000

DIN 51581

Foaming resistance

Foaming propensity:

  • in the temp. of25oC
  • in the temp. of95oC
  • in the temp. of25oC after the temp. of95oC

Foam stability:

  • in the temp. of25oC
  • in the temp. of95oC
  • in the temp. of25oC after the temp. of95oC

 

 

ml

ml

ml

 

ml

ml

ml

 

 

 

 

250

25

250

 

0

0

0

 

 

 

 

 

PN-85/C04055

Colour not higher than

Standard number

 

1

0,5

PN-80/C-04034

ASTM D 1500

Density in the temp. of15oC

g/cm3

 

 

0,864

PN EN ISO 12185

ASTM D 4052